YAOYU VAUTID 100 wear resistance steel plate prolong machine parts working time

The wear damage carries to replace machine parts causing a huge lost in the valuable time of productions. YaoYu VAUTID 100 wear resistance steel plate can convince our customers with high quality and long service lifetime as it has passed ASTM G65 abrasion test. Abrasion test results are reported as volume loss in cubic millimeters for the particular test procedure specified.
Materials of higher abrasion resistance will have a lower volume loss. YaoYu will send you test report for reference if you have any interests.

VAUTID 100 welding material chemical composition analysis:

C	Cr	Si	Mn	Ni	B	Fe
4.2~5.45%	25.3~30%	0.7~1.5%	0.2~1%	0.1~0.4%	1~1.5%	balance

Hardness of wear plate: HRC 58-62
Weld thicknesses over 6 mm are to be produced in multiple layers
Using open arc welding process, the weld layer offers a continuous wear resistance over the entire surface and also throughout the depth of the coating.
Quality of the hard weld seam
Discontinuities in the hard weld layer are unacceptable
Cracks in the basic material are unacceptable, but very common on hardfacing layer, as it is caused by stress relief.